Development and performance evaluation of tungsten carbide based self lubricating cutting tool

Show simple item record

dc.contributor.author Muthuraja, A
dc.date.accessioned 2017-11-27T10:14:09Z
dc.date.available 2017-11-27T10:14:09Z
dc.date.issued 2016
dc.identifier.other ROLL NO.10610330
dc.identifier.uri http://gyan.iitg.ernet.in/handle/123456789/863
dc.description Supervisor: S. Senthilvelan en_US
dc.description.abstract In manufacturing industries, major attention has been given to the dry machining due to the harmful effect and difficult handling of cutting fluids. This thesis intends to develop a solid lubricant cutting tool for carrying out dry machining. Tungsten carbide (WC) is considered for cutting tool material and calcium fluoride (CaF2) is considered for solid lubricant and powder metallurgy as a method for developing cutting tool material. The various amount of CaF2 (0-10 wt.%) were milled with tungsten carbide along with 10 wt.% of cobalt binder. Superior relative density (94 %) is achieved at 40 h of milling time and 400 MPa pressure. Compacted materials were subsequently sintered up to 1450 C under nitrogen atmosphere in a tube furnace. The fractured surface of the considered materials confirmed that material with 5 and 7 wt.% of CaF2 exhibited superior bonding between carbide particles.Considered material with 5 wt.% CaF2 exhibited superior hardness (85 HRA) and transverse rupture strength (1500 MPa) while compressed at 400 MPa. Developed materials were made to slide over the silicon carbon abrasive sheet and sintered disc with various normal loads and at a sliding speed. Under both abrasive and adhesive conditions, material with 5 wt.% CaF2 exhibited superior wear resistance and the lowest friction coefficient. The measured net surface temperature of the test specimen also confirmed this fact. The worn out test surface and the counter material surface revealed, traces of calcium and fluoride. Plain WC and WC with 5 wt.% CaF2 materials were considered to understand the cutting tool performance. WC-Co-5 wt.% CaF2 cutting tool generated 20-40 % lesser cutting force and 15-18 % lesser flank wear. Curlier and the smaller saw tooth of chip generated from WC-Co-5 wt. % CaF2 cutting tool confirmed the lesser heat generation in cutting and improved surface finish of the machined surface. en_US
dc.language.iso en en_US
dc.relation.ispartofseries TH-1614;
dc.subject MECHANICAL ENGINEERING en_US
dc.title Development and performance evaluation of tungsten carbide based self lubricating cutting tool en_US
dc.type Thesis en_US